P-02 1K Epoxy Block Filler/Paint
P-02
Product Overview
P-02 is a revolutionary, single component, acrylic block filler. It has excellent adhesion to concrete and provides fast dry and early hardness properties.
Uses
P-02 is most often used as a concrete block filler but can also be used as a vertical primer on concrete and wallboard, as a bodycoat and as a finish coat. It has good UV resistance and has very low odor. It is easy to apply and provides an excellent base layer for subsequent coatings of all types.
Preparation
The preparation method for each project is determined by a full understanding of the substrate to be coated, the chemistry of the coating system being used, the coating system thickness, and numerous other factors. The coating installer should fully read and understand ICRI Guideline NO.03732 and OSHA 29 CFR 1926.1153 before starting preparatory work. The aim, of preparing a substrate for coating applications, is to roughen the surface, remove weak layers, contaminants, dirt, debris and present a solid, clean, dry substrate for the primer. If unsure as to the level of preparation needed contact Polymer Nation at lab@polymernation.com.
The data below represents the most pertinent information needed by a professional installer to understand and efficiently install this material. The data was gathered at temperatures of 72-75 F and 30-50% RH. A wide array of independent and company test data has been compiled on this product but is too large to place on this Technical Data Sheet. Please direct inquiries for detailed test reports on this product to lab@polymernation.com.
P-02
| Description | Results | Notes |
| Kit Yield in Gallons | 5, | Material can be supplied in larger packaging upon request and with minimum quantities |
| Number of Components | 1 | |
| Mix Ratio Liquids by Volume | N/A | Stir the entire content prior to use to insure complete and even mixture |
| Ideal Application Temperatures | 60F-90F | Verify that substrate temperature is above 5 degrees of dewpoint during application and cure of material to avoid a potential amine blush |
| Viscosity in cP@25C/77F | 2200 | Warmer temperatures will reduce viscosity and lower temperatures will increase viscosity |
| Gel Time | N/A | Warmer temperatures will decrease gel time and lower temperatures will increase gel time |
| Dry to Touch | 30 min. | Warmer temperatures will reduce time and colder temperatures will increase time |
| Through Dry | 1 Hour | Warmer temperatures will reduce time and colder temperatures will increase time |
| Dry to Walk | N/A | Warmer temperatures will reduce time and colder temperatures will increase time |
| Dry to Lightly Use | 24 Hours | Warmer temperatures will reduce time and colder temperatures will increase time |
| Full Cure | 7 Days | Warmer temperatures will reduce time and colder temperatures will increase time |
| Pendulum (König) Hardness at 24 hours | 20 | Warmer temperatures will increase hardness |
| Pendulum (König) Hardness at 7 days | 40 | Warmer temperatures will shorten time to reach full hardness |
| Gloss @ 60 Degree Angle | 55-60 | |
| VOC’s of Mixed Material | <50 g/L | EPA Method 24 |
| Color Scale per ASTM D1500 | N/A | Clear to slightly amber before colorants are introduced |
| Solids by Volume Mixed | >58% | |
| Storage | 60F-90F | Store material between 60-90 degrees F in a protected dry location. |
| Odor | Subtle | Measuring odor offensiveness is difficult so experience with chemicals has been consulted here |
| Application Thickness in Mils | As a block-filler 10-12. As a body coat 6-8. | |
| Disposal | Dispose of material, containers, solvents, etc. per Federal, State and local guideline, rules and laws | |
| Available Colors | White | |
| Mixing & Installation | Stir entire container at 350 RPM for 2-3 minutes using an appropriate mixing blade and making sure not to introduce excessive air into the solution. Apply using airless equipment or brush and roll techniques. Recoat within 24 hours. Clean tools with a solvent similar to Xylene or Acetone. | |
| Polymer Nation believes the information contained herein to be true and accurate. Information contained herein is for evaluation purposes only. |
||