SP-41 Clear Flexible Polyaspartic
SP-41
Product Overview
SP-41 combines our robust, clear polyaspartic resin with our proprietary Iso blend to create a flexible, polyaspartic with uncanny performance characteristics. SP-41 is a 100% solids, low viscosity polyaspartic that provides amazing working time, abrasion and UV resistance.
Uses
SP-41 is primarily used as a clear topcoat over EPDM, due to its unsurpassed UV, flexibility and abrasion resistance. It can also be used as a component in flexible wall systems and padding. It adheres well to many substrates including concrete, gypsum, cement board, metals and fiberglass.
Preparation
The preparation method for each project is determined by a full understanding of the substrate to be coated, the chemistry of the coating system being used, the coating system thickness, and numerous other factors. The coating installer should fully read and understand ICRI Guideline NO.03732 and OSHA 29 CFR 1926.1153 before starting preparatory work. The aim, of preparing a substrate for coating applications, is to roughen the surface, remove weak layers, contaminants, dirt, debris and present a solid, clean, dry substrate for the primer. If unsure as to the level of preparation needed contact Polymer Nation at lab@polymernation.com.
The data below represents the most pertinent information needed by a professional installer to understand and efficiently install this material. The data was gathered at temperatures of 72-75 F and 30-50% RH. A wide array of independent and company test data has been compiled on this product but is too large to place on this Technical Data Sheet. Please direct inquiries for detailed test reports on this product to lab@polymernation.com.
SP-41
| Description | Results | Notes |
| Kit Yield in Gallons | 2, 10, 100 | Special packaging is available based on size of order and time constraints |
| Number of Components | 2 | |
| Mix Ratio Liquids by Volume | 1:1 | It is always preferred to mix the entire kit, whenever possible, to avoid off-ratio mixtures |
| Ideal Application Temperatures | 70F-80F 40-60% RH | Verify that substrate temperature is above 5 degrees of dewpoint during application and cure of material to avoid a potential amine blush |
| Mixed Viscosity in cP@25C/77F | 500-600 | Warmer temperatures will reduce viscosity and lower temperatures will increase viscosity |
| Gel Time | N/A | Warmer temperatures will decrease gel time and lower temperatures will increase gel time |
| Dry to Touch | 4 hours | Warmer temperatures will reduce time and colder temperatures will increase time |
| Through Dry | 11 Hours | Warmer temperatures will reduce time and colder temperatures will increase time |
| Dry to Walk | 16 Hours | Warmer temperatures will reduce time and colder temperatures will increase time |
| Dry to Lightly Use | 18 Hours | Warmer temperatures will reduce time and colder temperatures will increase time |
| Full Cure | 7 Days | Warmer temperatures will reduce time and colder temperatures will increase time |
| Pendulum Hardness (König) at 24 hrs. | 12 | Warmer temperatures will increase hardness |
| Pendulum Hardness (König) at 7 days | 50 | Warmer temperatures will shorten time to reach full hardness |
| Gloss @ 60 Degree Angle | 90+ | |
| VOC’s of Mixed Material | <50g/L | EPA Method 24 |
| Color Scale per ASTM D1500 | N/A | |
| Solids by Volume Mixed | 92.5% | |
| Storage | 60F-90F | Store material between 60-90 degrees F in a protected dry location. |
| Odor | Very Subtle | |
| Application Thickness in Mils | As a floor topcoat 6-12. As a wall topcoat 4-6. | |
| Disposal | Dispose of material, containers, solvents, etc.per Federal, State and local guideline, rules and laws | |
| Available Colors | Clear and Color Packs | |
| Mixing & Installation | Combine all of part A and B into a single container, large enough to accept the entire kit. Mix at 350 RPM for 2-3 minutes using an appropriate mixing blade and making sure not to introduce excessive air into the solution. Pour the entire content from the container onto the floor and follow normal squeegee and back roll or cut and roller techniques. Recoat within 24 hours. Clean tools with a solvent similar to Xylene or Acetone. | |
| Polymer Nation believes the information contained herein to be true and accurate. Information contained herein is for evaluation purposes only. | ||