F-60

F-60 Standard Speed Pigmented Polyaspartic

F-60

Product Overview

F-60 combines a proprietary blend of polyol with Iso to create an intermediate speed, pigmented polyaspartic. F-60 is a 83% solids, low viscosity polyaspartic that provides easy application with a moderately fast dry time. It will not yellow or chalk over time and provides great opacity which makes it is easy to create a solid looking finish with as little as 6 mils WFT.

Uses

F-60 is primarily used as a moderately fast setting, pigmented topcoat due to its unsurpassed UV and abrasion resistance. It can be applied to floors and walls and adheres well to many substrates including concrete, gypsum, cement board, metals and fiberglass.

Preparation

The preparation method for each project is determined by a full understanding of the substrate to be coated, the chemistry of the coating system being used, the coating system thickness, and numerous other factors. The coating installer should fully read and understand ICRI Guideline NO.03732 and OSHA 29 CFR 1926.1153 before starting preparatory work. The aim, of preparing a substrate for coating applications, is to roughen the surface, remove weak layers, contaminants, dirt, debris and present a solid, clean, dry substrate for the primer. If unsure as to the level of preparation needed contact Polymer Nation at lab@polymernation.com.

The data below represents the most pertinent information needed by a professional installer to understand and efficiently install this material. The data was gathered at temperatures of 72-75 F and 30-50% RH. A wide array of independent and company test data has been compiled on this product but is too large to place on this Technical Data Sheet. Please direct inquiries for detailed test reports on this product to lab@polymernation.com.

F-60

Description Results Notes
Kit Yield in Gallons 3, 15, 165 Special packaging is available based on size of order and time constraints
Number of Components 2
Mix Ratio Liquids by Volume 2:1 It is always preferred to mix the entire kit, whenever possible, to avoid off-ratio mixtures
Ideal Application Temperatures  70F-80F 40-60% RH
Mixed Viscosity in cP@25C/77F 600-700 Warmer temperatures will reduce viscosity and lower temperatures will increase viscosity
Gel Time N/A Warmer temperatures will decrease gel time and lower temperatures will increase gel time
Dry to Touch 4-5 hours Warmer temperatures will reduce time and colder temperatures will increase time
Through Dry 10-12 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Dry to Walk 14 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Dry to Lightly Use 18 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Full Cure 7 Days Warmer temperatures will reduce time and colder temperatures will increase time
Pendulum Hardness (König) at 24 hrs. 18 Warmer temperatures will increase hardness
Pendulum Hardness (König) at 7 days 50 Warmer temperatures will shorten time to reach full hardness
Gloss @ 60 Degree Angle 90+
VOC’s of Mixed Material  <50g/L EPA Method 24
Color Scale per ASTM D1500 N/A
Solids by Volume Mixed 92+%
Storage 60F-90F Store material between 60-90 degrees F in a protected dry location.
Odor Very Subtle
Application Thickness in Mils As a floor topcoat 6-12. As a wall topcoat 4-6.
Disposal Dispose of  material, containers, solvents, etc.per Federal, State and local guideline, rules and laws
Available Colors White, Light Gray, Warm Sun
Mixing & Installation Combine all of part A and B into a single container, large enough to accept the entire kit. Mix at 350 RPM for 2-3 minutes using an appropriate mixing blade and making sure not to introduce excessive air into the solution. Pour the entire content from the container onto the floor and follow normal squeegee and back roll or cut and roller techniques. Recoat within 24 hours. Clean tools with a solvent similar to Xylene or Acetone.
Polymer Nation believes the information contained herein to be true and accurate. Information contained herein is for evaluation purposes only.